The bonding strength between bone and α-2-cyanoacrylate polymers, with or without the addition of powdered hydroxyapatite, was determined. The tensile strength of a bone-cyanoacrylatebond was measured for each polymer: 4.31± 0.88 M Pa(methyl-), 5.74 ± 0.62 MPa (ethyl-), and 8.33 ± 0.41 MPa (isobutyl-). The tensile strength of the isobutyl-2-cyanoacrylatebond increased to 12.03 ± 0.72 MPa with the addition of 10% (w/v) hydroxyapatite before decreasing to 7.89 ± 0.58 Mpa on addition of 15% (w/v)hydroxyapatite.